Bonded niobium silicide and molybdenum silicide composite articles using brazes

ABSTRACT

An article, such as an airfoil having a melting temperature of at least about 1500° C. and comprising a first piece and a second piece joined by a braze to the first piece. The first piece comprises one of a first niobium-based refractory metal intermetallic composite and a first molybdenum-based refractory metal intermetallic composite, and the second piece comprises one of a second niobium-based refractory metal intermetallic composite and a second molybdenum-based refractory metal intermetallic composite. The braze joining the first piece to the second piece comprises a first metallic element and a second metallic element, wherein the first metallic element is one of titanium, palladium, zirconium, niobium, and hafnium, and wherein the second metallic element is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, the first metallic element being different from the second metallic element. This abstract is submitted in compliance with 37 C.F.R. 1.72( b ) with the understanding that it will not be used to interpret or limit the scope of or meaning of the claims.

BACKGROUND OF THE INVENTION

[0001] This application generally relates to composite articles that are joined together using brazes. More particularly, the invention described herein relates to bonded niobium-based silicide and molybdenum-based silicide composite articles that are joined together using brazes.

[0002] Nickel (Ni)-based superalloys have been used as jet engine materials for many years. The surface temperatures at the hottest locations of state-of-the-art jet engine turbine airfoils now approach 1,150° C., which is approximately 85% of the melting temperatures of Ni-based superalloys. Niobium (Nb) and molybdenum (Mo) based refractory metal intermetallic composites (hereinafter referred to as “Nb-based RMICs” and “Mo-based RMICs,”) have much higher potential application temperatures, provided that they can be used at approximately 80% or more of their melting temperatures, which are generally greater than about 1700° C.

[0003] Complex silicide-based RMICs that are made from Nb—Si—Ti—Hf—Cr—Al alloys or Mo—Si—B—Cr alloys appear to have the potential to become the next generation turbine materials with a long term, high-temperature capability that is significantly higher than that of current Ni-based superalloys. Because of their high melting temperatures, however, direct casting of hollow engine components with cooling channels from these Nb- and Mo-based RMICs is expected to be very difficult. At such high temperatures, very few materials can serve as casting cores and molds without experiencing creep, cracking, or reactions with the molten metals and thus contaminating the melt and degrading the cores. One potential alternative technique for the manufacture of complex-shaped components (e.g. airfoils) with cooling channels is to bond together, typically using brazes, two or more structural members that have been machined to the appropriate shapes. Currently, however, no such braze materials exist for these Nb- and Mo-based RMICs.

[0004] It is known in the art to make hollow components, such as turbine blades, by joining and bonding halves or multiple pieces together. However, the prior-art braze materials that have been developed for Ni-based or Fe-based alloys are not suitable for use with the new Nb- and Mo-based RMICs, which have very different alloy compositions and much higher working temperatures. Detrimental interactions are known to occur between nickel brazes, for example, and Nb-based RMICs.

[0005] Accordingly, there is a need in the art for improved high temperature composite articles that are joined together using brazes.

BRIEF SUMMARY OF THE INVENTION

[0006] The present invention meets this and other needs by providing articles formed from Nb- and Mo-based RMICs that are joined together by a braze. Brazes for joining Nb- and Mo-based RMICs are also disclosed.

[0007] Accordingly, one aspect of the invention is to provide an article having a melting temperature of at least about 1500° C. The article comprises a first piece and a second piece joined by a braze to the first piece. The first piece comprises one of a first Nb-based RMIC and a first Mo-based RMIC, wherein the first Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the first Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron. The second piece comprises one of a second Nb-based RMIC and a second Mo-based RMIC, wherein the second Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the second Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron.

[0008] A second aspect of the invention is to provide an airfoil having a melting temperature of at least about 1500° C. The airfoil comprises a first piece and a second piece joined by a braze to the first piece. The first piece comprises one of a first Nb-based RMIC and a first Mo-based RMIC, wherein the Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the first Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron. The second piece comprises one of a second Nb-based RMIC and a second Mo-based RMIC, wherein said second Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the second Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron.

[0009] A third aspect of the invention is to provide an airfoil having a melting temperature of at least about 1500° C. and comprising a first piece and a second piece joined by a braze to the first piece. The first piece comprises one of a first Nb-based RMIC and a first Mo-based RMIC, wherein the Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the first Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron. The second piece comprises one of a second Nb-based RMIC and a second Mo-based RMIC, wherein the second Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the second Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron. The braze joining the first piece to the second piece comprises a first metallic element and a second metallic element, wherein the first metallic element is one of titanium, palladium, zirconium, niobium, and hafnium, the second metallic element is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, and wherein the first metallic element is different from the second metallic element.

[0010] A fourth aspect of the invention is to provide a turbine assembly having at least one component. The at least one component has a melting temperature of at least about 1500° C. and comprises a first piece and a second piece joined by a braze to the first piece. The first piece comprises one of a first Nb-based RMIC and a first Mo-based RMIC, wherein the Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the first Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron. The second piece comprises one of a second Nb-based RMIC and a second Mo-based RMIC, wherein the second Nb-based RMIC comprises titanium, hafnium, silicon, chromium, and niobium, and the second Mo-based RMIC comprises molybdenum, silicon, and at least one of chromium and boron. The braze joining the first piece to the second piece comprises a first metallic element and a second metallic element, wherein the first metallic element is one of titanium, palladium, zirconium, niobium, and hafnium, the second metallic element is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, and wherein the first metallic element is different from the second metallic element.

[0011] Finally, a fifth aspect of the invention is to provide a method of making an article having a melting temperature of at least about 1500° C. and comprising a first piece and a second piece that are joined together by a braze. The first piece and second piece each comprise one of a niobium based refractory intermetallic composite and a molybdenum silicide based composite, wherein the niobium based refractory intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium and the molybdenum silicide based composite comprises molybdenum, silicon, and at least one of chromium and boron. The method comprises the steps of: providing the first piece and the second piece such that the first piece and the second piece form a an interface therebetween; providing a braze to the interface between the first piece and the second piece, the braze having a melting temperature and comprising a first metallic element and a second metallic element, the first metallic element one of titanium, palladium, zirconium, niobium, and hafnium, and the second metal one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, wherein the first metallic element is different from the second metallic element; heating the first piece, the second piece, and the braze to a first temperature for a first predetermined hold time, the first temperature being at least about 20° C. above the melting temperature of the braze; and further heating the first piece, the second piece, and the braze to a temperature up to about 1450° C. for a second predetermined hold time, thereby joining the first piece and the second piece at the interface and forming the article.

[0012] These and other aspects, advantages, and salient features of the present invention will become apparent from the following detailed description, the accompanying drawings, and the appended claims.

LIST OF FIGURES

[0013]FIG. 1 is a schematic illustration of a brazed article in accordance with one embodiment of the present invention;

[0014]FIG. 2 is a plot of approximate temperature regimes of the brazing and homogenization operations relative to the melting temperatures and the potential working temperatures of Nb- and Mo-based RIMCs; and

[0015]FIG. 3 is a method flow chart in accordance with one embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0016] In the following description, like reference characters designate like or corresponding parts throughout the several views shown in the figures. It is also understood that terms such as “top,” “bottom,” “outward,” “inward,” and the like are words of convenience and are not to be construed as limiting terms.

[0017] Referring to the drawings in general and to FIG. 1 in particular, it will be understood that the illustrations are for the purpose of describing a preferred embodiment of the invention and are not intended to limit the invention thereto.

[0018] An article 10, such as an airfoil, that is adapted for exposure to high-temperature conditions, typically greater than about 1000° C., includes a first piece 12 and a second piece 14, as shown in FIG. 1. In an exemplary embodiment, article 10 is an airfoil, for example a double-walled airfoil, for use within a hot gas path of a turbine assembly. Article 10 may be a component, such as a diffuser, casing, seal ring structure, or the like that is intended for use in a turbine assembly or any other structure in which temperatures in excess of about 1000° C. are encountered. Article 10 has a melting temperature of at least about 1500° C. Preferably, article 10has a melting temperature of at least about 1700° C.

[0019] First piece 12 is made of a first niobium based refractory metal intermetallic composite (hereinafter referred to as “Nb-based RMIC”) or a first molybdenum silicide based refractory metal intermetallic composite (hereinafter referred to as “Mo-based RMIC”). The first Nb-based RMIC typically comprises titanium, hafnium, silicon, chromium, and niobium and first Mo-based RMIC typically comprises molybdenum, silicon, and at least one of chromium and boron.

[0020] Second piece 14 is joined by a braze 16 to first piece 12. Second piece 14 is made of a second Nb-based RMIC or a second Mo-based RMIC. The second Nb-based RMIC typically comprises titanium, hafnium, silicon, chromium, and niobium, and the second Mo-based RMIC typically comprises molybdenum, silicon, and at least one of chromium and boron.

[0021] The Nb-based RMICs that are used to form the article 10 of the present invention possess a good balance of oxidation resistance and mechanical properties. The Nb-based RMICs preferably have compositions in the range of: between about 20 and about 30 atomic percent titanium; between about 13 and about 20 atomic percent silicon; between about 2 and about 10 atomic percent hafnium; between about 1 and about 12 atomic percent chromium; between about 1 and about 3 atomic percent aluminum; and between about 5 and about 7 atomic percent boron; with the balance comprising niobium. In order to provide even greater oxidation resistance, these alloys may optionally contain greater amounts of chromium and aluminum. In addition, the Nb-based RMICs may further include up to about 4 atomic percent Ge, and up to about 6 atomic percent each of Mo, Ta, V, W, Fe, Sn, and Zr.

[0022] In the present invention, the Mo-based RMICs that are used to form the article 10are based on molybdenum silicides, such as, but not limited to, MoSi₂, Mo₃Si, Mo₅Si₃, and Mo₅SiB₂ and comprise molybdenum, silicon, and at least one of boron or chromium. The Mo-based RMICs preferably comprise between about 2.5 and about 13.5 atomic percent silicon, between about 3.5 and about 26.5 atomic percent boron, and a balance of molybdenum. Alternatively, the Mo-based RMICs may comprise between about 13 and about 16 atomic percent silicon, between about 25 and about 40 atomic percent chromium, and a balance of molybdenum. The Mo-based RMICs may also include other elements, such as, but not limited to, tantalum, titanium, zirconium, rhenium, carbon, hafnium, germanium, tungsten, vanadium, tin, and aluminum.

[0023] The joints formed by braze 16 at interface 18 in article 10 must sustain thermal, axial/centrifugal, and pressure differential stresses. In an airfoil, for example, the gas path side of the article (formed by second piece 14 in FIG. 1) may experience temperatures of about 1315° C., whereas the cold side (formed by first piece 12 in FIG. 1) may only reach about 1000° C. Both steady-state and transient (during aircraft takeoffs and landings) thermal stresses thermal stresses act upon the bonding surfaces in shear mode. The pressure differential between the gas path side and the cold side can be as high as about 0.1 ksi, and it will exert ballooning, or tensile, stresses on the bonding surfaces at interface 18. In addition, the airfoils also produce centrifugal stresses during rotation that act upon the bonding surface in a shear mode. The combined stresses acting on the bonding surfaces can be very significant at the potentially high operating temperatures of a turbine assembly. The joints formed by braze 16 at interface 18 must sustain such stresses.

[0024] The interaction between braze 16, first piece 12, and second piece 14 must also be considered. The braze 16 must not significantly degrade the properties of the Nb- and/or Mo-based RMICs that form first piece 12 and second piece 14; it is preferable that braze 16 consume as little of first piece 12 and/or second piece 14 as is practical. Moreover, the braze 16 must have enough oxidation and environmental resistance to avoid internal oxidation during the brazing and subsequent homogenization processes.

[0025] Temperature regimes for the bonding operations also impose constraints on selection of braze 16 for joining first piece 12 and second piece 14. Preferably, braze 16 can be used for joining first piece 12 and second piece 14 at temperatures lower than about 1450° C. Bonding of first piece 12 and second piece 14 at temperatures higher than about 1450° C. requires expensive tooling and fixtures that may not be able to produce article 10 having the required precision in dimensions. In addition, internal oxidation becomes a severe threat to a good bonding at higher temperatures. On the other hand, when the braze 16 has a melting temperature below the potential operating temperatures (e.g., about 1000° C.) of article 10, care must be taken to ensure that low eutectic compositions of braze 16 with either first piece 12 or second piece 14 do not exist after homogenization of the interface.

[0026] Interdiffusion of elements from the braze 16 into first piece 12 and second piece 14 enhances joining of first piece 12 and second piece 14 by braze 16. Thus, the solubility of the elements of braze 16 in the Nb-based and/or Mo-based RIMCs must also be taken into account. After brazing and homogenization, the bonded and diffused regions of article 10 preferably have melting temperatures of up to about 1450° C. In service, joints formed by braze 16 at interface 18 in article 10 are exposed to temperatures that are close to the bulk temperature of article 10, or up to about 1200° C., rather than the temperature of up to about 1315° C. that is experienced by the surface (formed by second piece 14 in FIG. 1) of article 10. The approximate temperature regimes of the brazing and homogenization operations relative to the melting temperatures and the potential working temperatures of Nb- and Mo-based RIMCs are summarized in FIG. 2.

[0027] Braze 16 is typically made of first metal and a second metal. The first metal is a metallic element selected from one of titanium, palladium, zirconium, niobium, and hafnium. The second metallic element is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt. Although elements such as palladium, platinum, gold, zirconium, iron, nickel, cobalt, and the like are not components of the Nb- and Mo-based RMICs, these elements have good solubility in the metal bcc phase, and thus promote formation of the metal phase, which in turn enhances braze joint ductility and toughness.

[0028] In a first embodiment, braze 16 comprises between about 30 to about 90 atomic percent titanium with the balance comprising a metal selected from the group consisting of palladium, platinum, gold, chromium, cobalt, nickel, and iron. Braze 16 may further include at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, palladium, platinum, gold, aluminum, chromium, boron, zirconium, iron, cobalt, nickel, and vanadium, wherein the at least one additional element comprises up to 20 atomic percent of braze 16. The at least one additional element is different from the first metallic element and second metallic element.

[0029] In one preferred embodiment, braze 16 comprises between about 90 and about 55 atomic percent titanium with the balance comprising palladium. More preferably, braze 16 comprises between about 63 and about 73 atomic percent titanium with the balance comprising palladium.

[0030] In another preferred embodiment, braze 16 comprises between about 80 and about 30 atomic percent titanium with the balance comprising chromium. More preferably, braze 16 comprises between about 50 and about 60 atomic percent titanium with the balance comprising chromium.

[0031] In another preferred embodiment, braze 16 comprises between about 94 and about 74 atomic percent titanium with the balance comprising platinum. More preferably, braze 16 comprises between about 82 and about 86 atomic percent titanium with the balance comprising platinum.

[0032] In another preferred embodiment, braze 16 comprises between about 99 and about 59 atomic percent titanium with the balance comprising platinum. More preferably, braze 16 comprises between about 74 and about 84 atomic percent titanium with the balance comprising gold.

[0033] In another preferred embodiment, braze 16 comprises between about 58 and about 90 atomic percent titanium with the balance comprising cobalt. More preferably, braze 16 comprises between about 68 and about 78 atomic percent titanium with the balance comprising cobalt.

[0034] In another preferred embodiment, braze 16 comprises between about 90 and about 50 atomic percent titanium with the balance comprising cobalt. More preferably, braze 16 comprises between about 70 and about 80 atomic percent titanium with the balance comprising iron.

[0035] In another preferred embodiment, braze 16 comprises between about 50 and about 90 atomic percent titanium with the balance comprising nickel. More preferably, braze 16 comprises between about 71 and about 81 atomic percent titanium with the balance comprising nickel.

[0036] In a second embodiment, braze 16 comprises between about 20 and about 85 atomic percent palladium with the balance comprising one of chromium, aluminum, hafnium, zirconium, niobium, and vanadium. Braze 16 may further include at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, gold, aluminum, chromium, boron, zirconium, titanium, iron, nickel, cobalt, and vanadium, wherein the at least one additional element comprises up to 20 atomic percent of braze 16. The at least one additional element is different from the first metallic element and second metallic element.

[0037] In a preferred embodiment, braze 16 comprises between about 20 and about 80 atomic percent palladium with the balance comprising chromium. More preferably, braze 16 comprises between about 39 and about 49 atomic percent palladium with the balance comprising chromium.

[0038] In another preferred embodiment, braze 16 comprises between about 70 and about 86 atomic percent palladium with the balance comprising aluminum. More preferably, braze 16 comprises between about 75 and about 81 atomic percent palladium with the balance comprising aluminum.

[0039] In another preferred embodiment, braze 16 comprises between about 22 and about 32 atomic percent palladium with the balance comprising hafnium. More preferably, braze 16 comprises between about 25 and about 29 atomic percent palladium with the balance comprising hafnium.

[0040] In another preferred embodiment, braze 16 comprises between about 10 and about 35 atomic percent palladium with the balance comprising zirconium. More preferably, braze 16 comprises between about 22 and about 28 atomic percent palladium with the balance comprising zirconium.

[0041] In another preferred embodiment, braze 16 comprises between about 35 and about 60 atomic percent palladium with the balance comprising niobium. More preferably, braze 16 comprises between about 45 and about 49 atomic percent palladium with the balance comprising niobium.

[0042] In another preferred embodiment, braze 16 comprises between about 20 and about 60 atomic percent palladium with the balance comprising vanadium. More preferably, braze 16 comprises between about 36 and about 44 atomic percent palladium with the balance comprising vanadium.

[0043] In a third embodiment, braze 16 comprises between about 45 and about 90 atomic percent zirconium with the balance comprising one of platinum and vanadium. Braze 16 may further include at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, palladium, gold, aluminum, chromium, boron, titanium, iron, nickel, cobalt, and vanadium, wherein the at least one additional element comprises up to 20 atomic percent of braze 16. The at least one additional element is different from the first metallic element and second metallic element.

[0044] In a preferred embodiment, braze 16 comprises between about 68 and about 90 atomic percent zirconium with the balance comprising platinum. More preferably, braze 16 comprises between about 77 and about 81 atomic percent zirconium with the balance comprising platinum.

[0045] In another preferred embodiment, braze 16 comprises between about 45 and about 65 atomic percent zirconium with the balance comprising vanadium. More preferably, braze 16 comprises between about 55 and about 59 atomic percent zirconium with the balance comprising vanadium.

[0046] In a fourth embodiment, braze 16 comprises between about 15 and about 80 atomic percent niobium with the balance comprising one of iron, nickel, and cobalt. Braze 16 may further include at least one additional element selected from the group consisting of silicon, germanium, hafnium, palladium, platinum, gold, aluminum, chromium, boron, titanium, iron, nickel, cobalt, and vanadium, wherein the at least one additional element comprises up to 20 atomic percent of the first component of braze 16. The at least one additional element is different from the first metallic element and second metallic element.

[0047] In a preferred embodiment, braze 16 comprises between about 50 and about 80 atomic percent niobium with the balance comprising iron. More preferably, braze 16 comprises between about 62 and about 66 atomic percent niobium with the balance comprising iron.

[0048] In another preferred embodiment, braze 16 comprises between about 15 and about 50 atomic percent niobium with the balance comprising nickel. More preferably, braze 16 comprises between about 35 and about 45 atomic percent niobium with the balance comprising nickel.

[0049] In another preferred embodiment, braze 16 comprises between about 50 and about 71 atomic percent niobium with the balance comprising cobalt. More preferably, braze 16 comprises between about 59 and about 63 atomic percent niobium with the balance comprising cobalt.

[0050] In a fifth embodiment, the first component of braze 16 comprises between about 54 and about 74 atomic percent hafnium with the balance comprising iron. More preferably, braze 16 comprises between about 62 and about 64 atomic percent hafnium with the balance comprising iron. Braze 16 may further include at least one additional element selected from the group consisting of palladium, gold, niobium, aluminum, chromium, cobalt, nickel, boron, and vanadium, wherein the at least one additional element comprises up to 20 atomic percent of braze 16. The at least one additional element is different from the first metallic element and second metallic element.

[0051] Compositions of braze 16 are summarized in Table 1. TABLE 1 List of materials for first component of braze for joining Nb— and Mo— based RMICs based on binary metallic systems. Preferred braze More composition preferred range, composition at. % range, at. % Further additions, total amount up to 20 at. % Ti: 90-55 Ti: 67.5 ± 5 Ge, Si, Hf, Nb, Pt, Au, Al, Cr, B, Fe, Co, Ni Pd: 10-45 Pd: 32.5 ± 5 Cr: 80-20 Cr: 56 ± 5 Ge, Si, Al, Ti, Pt, Nb, Zr, V, Hf, Au, B, Fe, Co, Ni Pd: 20-80 Pd: 44 ± 5 V: 55-45 V: 43 ± 2 Ge, Si, Al, Ti, Nb, Cr, Hf, Pt, Pd, Au, B, Fe, Co, Ni Zr: 45-65 Zr: 57 ± 2 Pd: 70-86 Pd: 78 ± 3 Ge, Si, Ti, Nb, Cr, Zr, V, Hf, Pt, Au, B, Fe, Co, Ni Al: 30-14 Al: 21 ± 3 Ti: 80-30 Ti: 55 ± 5 Ge, Si, Al, Nb, Zr, V, Hf, Pt, Pd, Au, B, Fe, Co, Ni Cr: 20-70 Cr: 45 ± 5 Ti: 74-94 Ti: 84 ± 2 Ge, Si, Al, Cr, Nb, V, Hf, Pd, Au, B, Fe, Co, Ni Pt: 6-26 Pt: 16 ± 2 Pd: 22-32 Pd: 27 ± 2 Ge, Si, Al, Ti, Cr, Nb, Zr, V, Pt, Au, B, Fe, Co, Ni Hf: 78-68 Hf: 73 ± 2 Pd: 10-35 Pd: 25 ± 3 Ge, Si, Al, Ti, Cr, Nb, V, Hf, Pt, Au, B, Fe, Co, Ni Zr: 90-65 Zr: 75 ± 3 Pt: 10-32 Pd: 21 ± 2 Ge, Si, Al, Ti, Cr, Nb, V, Hf, Pd, Au, B, Fe, Co, Ni Zr: 90-68 Zr: 79 ± 2 Nb: 65-40 Nb: 53 ± 2 Ge, Si, Al, Ti, Cr, V, Hf, Pt, Au, B, Fe, Co, Ni Pd: 35-60 Pd: 47 ± 2 Pd: 20-60 Pd: 40 ± 4 Ge, Si, Al, Ti, Cr, Nb, Zr, Hf, Pt, Au, B, Fe, Co, Ni V: 80-40 V: 60 ± 4 Ti: 90-55 Ti: 79 ± 5 Ge, Si, Al, Nb, Cr, V, Hf, Pt, Pd, B, Fe, Co, Ni Au: 10-45 Au: 21 ± 5 Ti: 58-90 Ti: 73 ± 5 Ge, Si, Al, Nb, Cr, V, Hf, Pt, Pd, Au, B, Fe, Ni Co: 42-10 Co: 27 ± 5 Ti: 90-50 Ti: 70 ± 5 Ge, Si, Al, Nb, Cr, V, Hf, Pt, Pd, Au, B, Co, Ni Fe: 10-50 Fe: 30 ± 5 Ti: 90-50 Ti: 76 ± 5 Ge, Si, Al, Nb, Cr, V, Hf, Pt, Pd, Au, B, Fe, Co Ni: 10-50 Ni: 24 ± 5 Nb: 80-50 Nb: 64 ± 2 Ge, Si, Al, Ti, Cr, V, Hf, Pt, Pd, Au, B, Co, Ni Fe: 20-50 Fe: 36 ± 2 Nb: 15-50 Nb: 40.5 ± 5 Ge, Si, Al, Ti, Cr, V, Hf, Pd, Au, B, Fe, Co Ni: 85-50 Ni: 59.5 ± 5 Nb: 71-50 Nb: 61 ± 2 Ge, Si, Al, Ti, Cr, V, Hf, Pd, Au, B, Fe, Ni Co: 29-50 Co: 39 ± 2 Hf: 54-74 Hf: 64 ± 2 Al, Nb, Cr, V, Pd, Au, B, Co, Ni Fe: 46-26 Fe: 36 ± 2

[0052] A method 100 of making article 10 is shown in FIG. 2. First, in step S1, first piece 12 and second piece 14 are provided such that first piece 12 and second piece 14 form an interface 18 therebetween. Next, in step S2, braze 16 is provided to interface 18 between first piece 12 and second piece 14. Braze 16 may be provided to interface 18 as a foil, which is sandwiched between first piece 12 and second piece 14. In those instances where braze 16 is too brittle to be formed into a foil, either a powder tape or powder paste of braze 16 may be used to provide the braze 16 to the interface 18. Braze 16 includes a first metal and a second metal, the first metal is a metal selected from the group consisting of titanium, palladium, zirconium, niobium, and hafnium, and the second metal is a metal selected from the group consisting of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt.

[0053] Next, at step S3, first piece 12, second piece 14, and braze 16 are heated to a first temperature for a first predetermined hold time, the first temperature being at least 20° C. above the melting temperature of braze 16. Next, at step S4, first piece 12, second piece 14, and braze 16 are further heated to a temperature up to about 1450° C. for a second predetermined hold time, thereby joining first piece 12 and second piece 14 at interface 18 and forming article 10.

[0054] While typical embodiments have been set forth for the purpose of illustration, the foregoing description should not be deemed to be a limitation on the scope of the invention. Accordingly, various modifications, adaptations, and alternatives may occur to one skilled in the art without departing from the spirit and scope of the present invention. 

What is claimed is:
 1. An article having a melting temperature of at least about 1500° C., said article comprising: a) a first piece comprising one of a first niobium-based refractory metal intermetallic composite and a first molybdenum-based refractory metal intermetallic composite, wherein said first niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said first molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron; and b) a second piece joined by a braze to said first piece, said second piece comprising one of a second niobium-based refractory metal intermetallic composite and a second molybdenum-based refractory metal intermetallic composite, wherein said second niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said second molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron.
 2. The article according to claim 1, wherein said braze comprises a first metallic element and a second metallic element, wherein said first metallic element is one of titanium, palladium, zirconium, niobium, and hafnium, and wherein said second metal is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, and wherein said first metallic element is different from said second metallic element.
 3. The article according to claim 2, wherein said braze comprises between about 30 and about 90 atomic percent titanium with the balance comprising one of palladium, platinum, gold, chromium, cobalt, nickel, and iron.
 4. The article according to claim 3, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, palladium, platinum, gold, aluminum, chromium, boron, zirconium, iron, cobalt, nickel, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 5. The article according to claim 3, wherein said braze comprises between about 90 and about 55 atomic percent titanium and a balance of palladium.
 6. The article according to claim 5, wherein said braze comprises between about 63 and about 73 atomic percent titanium and a balance of palladium.
 7. The article according to claim 3, wherein said braze comprises between about 80 and about 30 atomic percent titanium and a balance of chromium.
 8. The article according to claim 7, wherein said braze comprises between about 50 and about 60 atomic percent titanium and a balance of chromium.
 9. The article according to claim 3, wherein said braze comprises between about 94 and about 74 atomic percent titanium and a balance of platinum.
 10. The article according to claim 9, wherein said braze comprises between about 82 and about 86 atomic percent titanium and a balance of platinum.
 11. The article according to claim 3, wherein said braze comprises between about 99 and about 59 atomic percent titanium and a balance of gold.
 12. The article according to claim 11, wherein said braze comprises between about 74 and about 84 atomic percent titanium and a balance of gold.
 13. The article according to claim 3, wherein said braze comprises between about 58 and about 90 atomic percent titanium and a balance of cobalt.
 14. The article according to claim 13, wherein said braze comprises between about 68 and about 78 atomic percent titanium and a balance of cobalt.
 15. The article according to claim 3, wherein said braze comprises between about 90 and about 50 atomic percent titanium and a balance of iron.
 16. The article according to claim 15, wherein said braze comprises between about 70 and about 80 atomic percent titanium and a balance of iron.
 17. The article according to claim 3, wherein said braze comprises between about 50 and about 90 atomic percent titanium and a balance of nickel.
 18. The article according to claim 17, wherein said braze comprises between about 71 and about 81 atomic percent titanium and a balance of nickel.
 19. The article according to claim 2, wherein said braze comprises between about 20 and about 85 atomic percent palladium with the balance comprising one of chromium, aluminum, hafnium, zirconium, niobium, and vanadium.
 20. The article according to claim 19, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, gold, aluminum, chromium, boron, zirconium, titanium, iron, nickel, cobalt, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 21. The article according to claim 19, wherein said braze comprises between about 20 and about 80 atomic percent palladium and a balance of chromium.
 22. The article according to claim 21, wherein said braze comprises between about 39 and about 49 atomic percent palladium and a balance of chromium.
 23. The article according to claim 19, wherein said braze comprises between about 70 and about 86 atomic percent palladium and a balance of aluminum.
 24. The article according to claim 23, wherein said braze comprises between about 75 and about 81 atomic percent palladium and a balance of aluminum.
 25. The article according to claim 19, wherein said braze comprises between about 22 and about 32 atomic percent palladium and a balance of hafnium.
 26. The article according to claim 25, wherein said braze comprises between about 25 and about 29 atomic percent palladium and a balance of hafnium.
 27. The article according to claim 19, wherein said braze comprises between about 10and about 35 atomic percent palladium and a balance of zirconium.
 28. The article according to claim 27, wherein said braze comprises between about 22 and about 28 atomic percent palladium and a balance of zirconium.
 29. The article according to claim 19, wherein said braze comprises between about 35 and about 60 atomic percent palladium and a balance of niobium.
 30. The article according to claim 29, wherein said braze comprises between about 45 and about 49 atomic percent palladium and a balance of niobium.
 31. The article according to claim 19, wherein said braze comprises between about 20 and about 60 atomic percent palladium and a balance of vanadium.
 32. The article according to claim 31, wherein said braze comprises between about 36 and about 44 atomic percent palladium and a balance of vanadium.
 33. The article according to claim 2, wherein said braze comprises between about 45 and about 90 atomic percent zirconium with the balance comprising one of platinum and vanadium.
 34. The article according to claim 33, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, palladium, gold, aluminum, chromium, boron, titanium, iron, nickel, cobalt, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 35. The article according to claim 33, wherein said braze comprises between about 68 and about 90 atomic percent zirconium and a balance of platinum.
 36. The article according to claim 35, wherein said braze comprises between about 77 and about 81 atomic percent zirconium and a balance of platinum.
 37. The article according to claim 33, wherein said braze comprises between about 45 and about 65 atomic percent zirconium and a balance of vanadium.
 38. The article according to claim 37, wherein said braze comprises between about 55 and about 59 atomic percent zirconium and a balance of vanadium.
 39. The article according to claim 2, wherein said braze comprises between about 15 and about 80 atomic percent niobium with the balance comprising one of iron, nickel, and cobalt.
 40. The article according to claim 39, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, palladium, platinum, gold, aluminum, chromium, boron, titanium, iron, nickel, cobalt, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 41. The article according to claim 39, wherein said braze comprises between about 50 and about 80 atomic percent niobium and a balance of iron.
 42. The article according to claim 41, wherein said braze comprises between about 62 and about 66 atomic percent niobium and a balance of iron.
 43. The article according to claim 39, wherein said braze comprises between about 15 and about 50 atomic percent niobium and a balance of nickel.
 44. The article according to claim 43, wherein said braze comprises between about 35 and about 45 atomic percent niobium and a balance of nickel.
 45. The article according to claim 39, wherein said braze comprises between about 50 and about 71 atomic percent niobium and a balance of cobalt.
 46. The article according to claim 45, wherein said braze comprises between about 59 and about 63 atomic percent niobium and a balance of cobalt.
 47. The article according to claim 2, wherein said braze comprises between about 54 and about 74 atomic percent hafnium with the balance comprising iron.
 48. The article according to claim 47, wherein said braze further comprises at least one additional element selected from the group consisting of palladium, gold, aluminum, niobium, chromium, cobalt, nickel, boron, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 49. The article according to claim 47, wherein said braze comprises between about 62 and about 64 atomic percent hafnium with the balance comprising iron.
 50. The article according to claim 1, wherein said melting temperature is at least about 1700° C.
 51. The article according to claim 1, wherein said first piece comprises said first niobium-based refractory metal intermetallic composite.
 52. The article according to claim 51, wherein said second piece comprises said second niobium-based refractory metal intermetallic composite.
 53. The article according to claim 1, wherein said first piece comprises said first molybdenum-based refractory metal intermetallic composite.
 54. The article according to claim 53, wherein said second piece comprises said second molybdenum-based refractory metal intermetallic composite.
 55. The article according to claim 1, wherein said article is one of an airfoil, a diffuser, a casing, and a seal ring structure.
 56. The article according to claim 55, wherein said article has a service temperature of at least about 1000° C.
 57. An airfoil having a melting temperature of at least about 1500° C., said airfoil comprising: a) a first piece comprising one of a first niobium-based refractory metal intermetallic composite and a first molybdenum-based refractory metal intermetallic composite, wherein said first niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said first molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron; and b) a second piece joined by a braze to said first piece, said second piece comprising one of a second niobium-based refractory metal intermetallic composite and a second molybdenum-based refractory metal intermetallic composite, wherein said second niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said second molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron.
 58. The airfoil according to claim 57, wherein said airfoil is a double-walled airfoil.
 59. The airfoil according to claim 57, wherein said airfoil is located in a hot gas path of a turbine assembly.
 60. The airfoil according to claim 57, wherein said melting temperature is at least about 1700° C.
 61. The airfoil according to claim 57, wherein said first piece comprises said first niobium-based refractory metal intermetallic composite.
 62. The airfoil according to claim 61, wherein said second piece comprises said second niobium-based refractory metal intermetallic composite.
 63. The airfoil according to claim 57, wherein said first piece comprises said first molybdenum-based refractory metal intermetallic composite.
 64. The airfoil according to claim 63, wherein said second piece comprises said second molybdenum-based refractory metal intermetallic composite.
 65. An airfoil having a melting temperature of at least about 1500° C., said airfoil comprising: a) a first piece comprising one of a first niobium-based refractory metal intermetallic composite and a first molybdenum-based refractory metal intermetallic composite, wherein said first niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said first molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron; and b) a second piece joined by a braze to said first piece, said second piece comprising one of a second niobium-based refractory metal intermetallic composite and a second molybdenum-based refractory metal intermetallic composite, wherein said second niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said second molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron, and wherein said braze comprises a first metallic element and a second metallic element, wherein said first metallic element is one of titanium, palladium, zirconium, niobium, and hafnium, and wherein said second metallic element is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, wherein said first metallic element is different from said second metallic element.
 66. The airfoil according to claim 65, wherein said braze comprises between about 30 and about 90 atomic percent titanium with the balance comprising one of palladium, platinum, gold, chromium, cobalt, nickel, and iron.
 67. The airfoil according to claim 66, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, palladium, platinum, gold, aluminum, chromium, boron, zirconium, iron, cobalt, nickel, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 68. The airfoil according to claim 66, wherein said braze comprises between about 90 and about 55 atomic percent titanium and a balance of palladium
 69. The airfoil according to claim 68, wherein said braze comprises between about 63 and about 73 atomic percent titanium and a balance of palladium.
 70. The airfoil according to claim 66, wherein said braze comprises between about 80 and about 30 atomic percent titanium and a balance of chromium.
 71. The airfoil according to claim 70, wherein said braze comprises between about 50 and about 60 atomic percent titanium and a balance of chromium.
 72. The airfoil according to claim 66, wherein said braze comprises between about 94 and about 74 atomic percent titanium and a balance of platinum.
 73. The airfoil according to claim 72, wherein said braze comprises between about 82 and about 86 atomic percent titanium and a balance of platinum.
 74. The airfoil according to claim 66, wherein said braze comprises between about 99 and about 59 atomic percent titanium and a balance of gold.
 75. The airfoil according to claim 74, wherein said braze comprises between about 74 and about 84 atomic percent titanium and a balance of gold.
 76. The airfoil according to claim 66, wherein said braze comprises between about 58 and about 90 atomic percent titanium and a balance of cobalt.
 77. The airfoil according to claim 76, wherein said braze comprises between about 68 and about 78 atomic percent titanium and a balance of cobalt.
 78. The airfoil according to claim 66, wherein said braze comprises between about 90 and about 50 atomic percent titanium and a balance of iron.
 79. The airfoil according to claim 78, wherein said braze comprises between about 70 and about 80 atomic percent titanium and a balance of iron.
 80. The airfoil according to claim 66, wherein said braze comprises between about 50 and about 90 atomic percent titanium and a balance of nickel.
 81. The airfoil according to claim 80, wherein said braze comprises between about 71 and about 81 atomic percent titanium and a balance of nickel.
 82. The airfoil according to claim 65, wherein said braze comprises between about 20 and about 85 atomic percent palladium with the balance comprising one of chromium, aluminum, hafnium, zirconium, niobium, and vanadium.
 83. The airfoil according to claim 82, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, gold, aluminum, chromium, boron, zirconium, titanium, iron, nickel, cobalt, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 84. The airfoil according to claim 82, wherein said braze comprises between about 20 and about 80 atomic percent palladium and a balance of chromium.
 85. The airfoil according to claim 84, wherein said braze comprises between about 39 and about 49 atomic percent palladium and a balance of chromium.
 86. The airfoil according to claim 82, wherein said braze comprises between about 70 and about 86 atomic percent palladium and a balance of aluminum.
 87. The airfoil according to claim 86, wherein said braze comprises between about 75 and about 81 atomic percent palladium and a balance of aluminum.
 88. The airfoil according to claim 82, wherein said braze comprises between about 22 and about 32 atomic percent palladium and a balance of hafnium.
 89. The airfoil according to claim 88, wherein said braze comprises between about 25 and about 29 atomic percent palladium and a balance of hafnium.
 90. The airfoil according to claim 82, wherein said braze comprises between about 10 and about 35 atomic percent palladium and a balance of zirconium.
 91. The airfoil according to claim 90, wherein said braze comprises between about 22 and about 28 atomic percent palladium and a balance of zirconium.
 92. The airfoil according to claim 82, wherein said braze comprises between about 35 and about 60 atomic percent palladium and a balance of niobium.
 93. The airfoil according to claim 92, wherein said braze comprises between about 45 and about 49 atomic percent palladium and a balance of niobium.
 94. The airfoil according to claim 82, wherein said braze comprises between about 20 and about 60 atomic percent palladium and a balance of vanadium.
 95. The airfoil according to claim 94, wherein said braze comprises between about 36 and about 44 atomic percent palladium and a balance of vanadium.
 96. The airfoil according to claim 65, wherein said braze comprises between about 45 and about 90 atomic percent zirconium with the balance comprising one of platinum and vanadium.
 97. The airfoil according to claim 96, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, palladium, gold, aluminum, chromium, boron, titanium, iron, nickel, cobalt, and vanadium, and wherein said at least one additional element comprises up to 20 atomic percent of said braze.
 98. The airfoil according to claim 96, wherein said braze comprises between about 68 and about 90 atomic percent zirconium and a balance of platinum.
 99. The airfoil according to claim 98, wherein said braze comprises between about 77 and about 81 atomic percent zirconium and a balance of platinum.
 100. The airfoil according to claim 96, wherein said braze comprises between about 45 and about 65 atomic percent zirconium and a balance of vanadium.
 101. The airfoil according to claim 100, wherein said braze comprises between about 55 and about 59 atomic percent zirconium and a balance of vanadium.
 102. The airfoil according to claim 65, wherein said braze comprises between about 15 and about 80 atomic percent niobium with the balance comprising one of iron, nickel, and cobalt.
 103. The airfoil according to claim 102, wherein said braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, palladium, platinum, gold, aluminum, chromium, boron, titanium, iron, nickel, cobalt, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 104. The airfoil according to claim 102, wherein said braze comprises between about 50 and about 80 atomic percent niobium and a balance of iron.
 105. The airfoil according to claim 104, wherein said braze comprises between about 62 and about 66 atomic percent niobium and a balance of iron.
 106. The airfoil according to claim 102, wherein said braze comprises between about 15 and about 50 atomic percent niobium and a balance of nickel.
 107. The airfoil according to claim 106, wherein said braze comprises between about 35 and about 45 atomic percent niobium and a balance of nickel.
 108. The airfoil according to claim 102, wherein said braze comprises between about 50 and about 71 atomic percent niobium and a balance of cobalt.
 109. The airfoil according to claim 108, wherein said braze comprises between about 59 and about 63 atomic percent niobium and a balance of cobalt.
 110. The airfoil according to claim 65, wherein said braze comprises between about 54 and about 74 atomic percent hafnium with the balance comprising iron.
 111. The airfoil according to claim 110, wherein said braze further comprises at least one additional element selected from the group consisting of palladium, gold, aluminum, niobium, chromium, cobalt, nickel, boron, and vanadium, and wherein said at least one additional element comprises up to about 20 atomic percent of said braze.
 112. The airfoil according to claim 110, wherein said braze comprises between about 62 and about 64 atomic percent hafnium with the balance comprising iron.
 113. The airfoil according to claim 65, wherein said airfoil is a double-walled airfoil.
 114. The airfoil according to claim 65, wherein said airfoil is located in a hot gas path of a turbine assembly.
 115. The airfoil according to claim 65, wherein said melting temperature is at least about 1700° C.
 116. The airfoil according to claim 65, wherein said first piece comprises said first niobium-based refractory metal intermetallic composite.
 117. The airfoil according to claim 116, wherein said second piece comprises said second niobium-based refractory metal intermetallic composite.
 118. The airfoil according to claim 65, wherein said first piece comprises said first molybdenum-based refractory metal intermetallic composite.
 119. The airfoil according to claim 118, wherein said second piece comprises said second molybdenum-based refractory metal intermetallic composite.
 120. A turbine assembly having at least one component, said at least one component having a melting temperature of at least about 1500° C. and comprising: a) a first piece comprising one of a first niobium-based refractory metal intermetallic composite and a first molybdenum-based refractory metal intermetallic composite, wherein said first niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said first molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron; and b) a second piece joined by a braze to said first piece, said second piece comprising one of a second niobium-based refractory metal intermetallic composite and a second molybdenum-based refractory metal intermetallic composite, wherein said second niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium, and said second molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron, and wherein said braze comprises a first metallic element and a second metallic element, wherein said first metallic element is one of titanium, palladium, zirconium, niobium, and hafnium, and wherein said second metallic element is one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, wherein said first metallic element is different from said second metallic element.
 121. The turbine assembly according to claim 120, wherein said at least one component is one of an airfoil, a diffuser, a casing, and a seal ring structure.
 122. The turbine assembly to claim 120, wherein said at least one component has a service temperature of at least about 1000° C.
 123. A method of making an article, the article having a melting temperature of at least about 1500° C. and comprising a first piece and a second piece that are joined together by a braze, wherein the first piece and second piece each comprise one of a niobium-based refractory metal intermetallic composite and a molybdenum-based refractory metal intermetallic composite, wherein the niobium-based refractory metal intermetallic composite comprises titanium, hafnium, silicon, chromium, and niobium and the molybdenum-based refractory metal intermetallic composite comprises molybdenum, silicon, and at least one of chromium and boron, the method comprising the steps of: a) providing the first piece and the second piece such that the first piece and the second piece form an interface therebetween; b) providing a braze to the interface between the first piece and the second piece, the braze having a melting temperature and comprising a first metallic element and a second metallic element, the first metallic element being one of titanium, palladium, zirconium, niobium, and hafnium, and the second metallic element being one of titanium, palladium, zirconium, niobium, hafnium, aluminum, chromium, vanadium, platinum, gold, iron, nickel, and cobalt, wherein the first metallic element is different from the second metallic element; c) heating the first piece, the second piece, and the braze to a first temperature for a first predetermined hold time, the first temperature being at least 20° C. above the melting temperature of the braze; and d) further heating the first piece, the second piece, and the braze to a temperature up to about 1450° C. for a second predetermined hold time, thereby joining the first piece and the second piece at the interface and forming the article.
 124. The method of claim 123, wherein the step of providing a braze to the interface between the first piece and the second piece comprises providing a braze comprising between about 30 and about 90 atomic percent titanium with the balance comprising one of palladium, platinum, gold, chromium, cobalt, nickel, and iron.
 125. The method of claim 12 4, wherein the braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, palladium, platinum, gold, aluminum, chromium, boron, zirconium, iron, cobalt, nickel, and vanadium, and wherein the at least one additional element comprises up to about 20 atomic percent of said braze.
 126. The method of claim 123, wherein the step of providing a braze to the interface between the first piece and the second piece comprises providing a braze comprising between about 20 and about 85 atomic percent palladium with the balance comprising one of chromium, aluminum, hafnium, zirconium, niobium, and vanadium.
 127. The method of claim 126, wherein the braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, gold, aluminum, chromium, boron, zirconium, titanium, and vanadium, and wherein the at least one additional element comprises up to about 20 atomic percent of said braze.
 128. The method of claim 123, wherein the step of providing a braze to the interface between the first piece and the second piece comprises providing a braze comprising between about 45 and about 90 atomic percent zirconium with the balance comprising one of platinum and vanadium.
 129. The method of claim 128, wherein the braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, niobium, platinum, palladium, gold, aluminum, chromium, boron, titanium, nickel, iron, cobalt, and vanadium, and wherein the at least one additional element comprises up to about 20 atomic percent of said braze.
 130. The method of claim 123, wherein the step of providing a braze to the interface between the first piece and the second piece comprises providing a braze comprising between about 15 and about 80 atomic percent niobium with the balance comprising one of iron, nickel, and cobalt.
 131. The method of claim 130, wherein the braze further comprises at least one additional element selected from the group consisting of silicon, germanium, hafnium, palladium, platinum, gold, aluminum, chromium, boron, titanium, iron, cobalt, nickel, and vanadium, and wherein the at least one additional element comprises up to about 20 atomic percent of said braze.
 132. The method of claim 123, wherein the step of providing a braze to the interface between the first piece and the second piece comprises providing a braze comprising between about 15 and about 80 atomic percent hafnium with the balance comprising iron.
 133. The method of claim 132, wherein the braze further comprises at least one additional element selected from the group consisting of palladium, gold, aluminum, niobium, chromium, cobalt, nickel, boron, and vanadium, and wherein the at least one additional element comprises up to about 20 atomic percent of said braze.
 134. The method of claim 123, wherein the article is one of an airfoil, a diffuser, a casing, and a seal ring structure.
 135. The method of claim 134, wherein the airfoil is a double-walled airfoil.
 136. The method of claim 123, wherein the article has a melting temperature of at least about 1700° C. 